Modelo: P20, 1.2311, 1.2312, 3Cr2Mo
Estándar: AiSi, ASTM, bs, ESTRUENDO, GB, JIS
Lugar De Origen: porcelana
Proceso De Producción: Laminado en caliente
Acero Especial: Molde de acero
Tolerancia: ± 1%
Servicio De Procesamiento: Doblado, Soldadura, Desenrollar, Puñetazos, Corte
| Unidades de venta | : | Ton |
| Ejemplo de una imagen | : |
|
The file is encrypted. Please fill in the following information to continue accessing it
Parametros del producto
1. Estándar internacional
| GB | DIN | ASIA | JIS |
| 3Cr2MnNi | 1.2311 | P20 | PDS-S |
| 1.2311 | C | Si | Mn | Cr | Mo | S | P |
| 0.35-0.45 | 0.20-0.40 | 0.60-1.00 | 1.80-2.10 | 0.30-0.55 | ≤0.003 | ≤0.003 |
| Flat Bar Size | Round Bar Size(mm) | ||||
| Thickness | Width | Length | Diameter | Length | |
| 10-700 | 155-2200 | 2000-6000 | 20-200 | 2000-6000 | |
4. Técnica de producto:
Introducción:
Los aceros de molde bajo de carbono o los aceros del grupo P son de diferentes tipos que incluyen los aceros P2, P3, P4, P5, P6, P20 y P21. El cromo y el níquel son los principales elementos de aleación que se encuentran en los aceros del Grupo P.
Los aceros de la herramienta P20 están nitruros o se carburan. Estos aceros son capaces de ser mecanizados en troqueles y moldes complejos y grandes. Los aceros P20 se usan principalmente en la condición carburizada. La presencia de cromo y níquel mejora la tenacidad y la dureza de los aceros P20.
| Tempering: | P20 tool steels are tempered at 482-593°C (900 to 1100°F) for a Rockwell C hardness of 28 to 34. |
| Annealing: | Annealing takes place at 760-788°C (1400 to 1450°F) and then the steels are cooled slowly in the furnace at a temperature less than 4°C (40°F) per hour. |
| Cold Working: | P20 tool steels are capable of being readily cold worked by using conventional tooling methods with the alloy in the annealed condition. |
| Welding: | Conventional methods are used for welding of P20 tool steels. |
| Forging: | P20 tool steels are forged at 1093°C (2000°F) down to 899°C (1650°F). Forging below 871°C (1600°F) is not recommended for these steels. |
| Forming: | P20 tool steels can be readily formed by conventional methods in the annealed condition. |
| Machinability: | P20 tool steels have excellent machinability at about 80% that of water hardening steels. |
| Heat Treatment: | P20 tool steels are heated to 871-899°C (1600-1650°F) in the carburizing medium during the carburizing process. After being carburized, these steels are heated to 816-871°C (1500-1600°F) in order to be hardened and then held for 15 minutes and finally oil quenched. |
| Applications: | P20 tool steels are used for low-temperature applications that include injection molds and die casting dies. |
Fábrica
Prueba de producto
Embalaje y envío
Contáctenos
Si tiene alguna pregunta, ¡no dude en ponerse en contacto conmigo por correo electrónico o teléfono!
Principalmente los productos cubren tubería de acero al carbono, tubería de acero galvanizado, tubería de acero sin costura, tubería de acero cuadrada, tubo de acero perfeccionado, tubería de acero de forma especial, alambre de hierro galvanizado y ángulo de acero, haz H, acero plano, acero redondo, acero de canal, etc. .
CONTÁCTENOS
Copyright © 2024 Todos los derechos reservados por Tianjin Youfa Steel Co., Ltd.
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Contact Now